مطالعه ی مشکلات موجود در فرآیند تولید پلی استایرن انبساطی و پیشنهاد اصلاحی برای رفع مساله کلوخه شدن محصول نهایی
Parallel Title Proper
Study of Difficulties in the Expanded Poly styrene coating process and suggestion to overcome Lumping of final product
First Statement of Responsibility
/علی اکبرعبدل زاده
.PUBLICATION, DISTRIBUTION, ETC
Name of Publisher, Distributor, etc.
: پردیس بین المللی ارس
Date of Publication, Distribution, etc.
، ۱۳۹۹
Name of Manufacturer
، عباسپور
PHYSICAL DESCRIPTION
Specific Material Designation and Extent of Item
۹۶ص
NOTES PERTAINING TO PUBLICATION, DISTRIBUTION, ETC.
Text of Note
چاپی - الکترونیکی
DISSERTATION (THESIS) NOTE
Dissertation or thesis details and type of degree
کارشناسی ارشد
Discipline of degree
مهندسی شیمی پلیمر
Date of degree
۱۳۹۹/۰۷/۳۰
Body granting the degree
تبریز
SUMMARY OR ABSTRACT
Text of Note
پلیاستایرن انبساطی یکی از محصولات حاصل از فنآوری فومشدن دانهای است .دانههای پلیاستایرن تولیدی، در مرحلهی طبقهبندی و غربال براساس اندازهی دانههای پلیاستایرن انبساطی به کسرهای مختلفی نظیر ۰۳۳ ، ۰۳۳، ۰۳۳،۹۳۳و۰۳۳ طبقهبندی شده و پس از پوششدهی و بستهبندی در اختیار شرکتهای صنایع پاییندست قرار میگیرند .وجود آلودگیهای معدنی، بارهای الکترواستاتیک و چسبندگی بین دانههای پلیاستایرن انبساطی باعث تجمع و کلوخهشدن دانهها در فرایند پیشانبساطی شده و مشکلاتی را در صنایع پاییندست به وجود میآورد .جهت جلوگیری از بههم چسبیدن دانهها و ممانعت از نفوذ عامل منبسطکننده به خارج از ساختار سلولی، از عوامل پوششدهنده استفاده میشود .برای بررسی اثر پوششدهندههایی نظیر استئارات مونو گلیسرول، استئارات روی و استئارات کلسیم بر روی کاهش میزان کلوخهشدهگی، غلظتهای وزنی ۳/۰ ،۳/۹و۳/۰ درصد از ترکیبات فوق، به۰۳ گرم از نمونههایی از پلیاستایرن گرید۰۳۳ و ۰۳۳ افزوده شد .تعداد۹۱ نمونهی تهیهشده، با شمارهگذاری از۹ تا ،۹۱بهطور کامل تحت آزمون کلوخهشدهگی) تست لامپینگ (قرار گرفتند .تمامی نمونهها در زمان واحد تهیهشده و تحت شرایط یکسان نگهداری شدند .نمونههای۳/۰ درصد وزنی از استئارات روی در۰۳ گرم از پلیاستایرن گرید(۰۳۳ نمونه ،)۶استئارات روی۳/۰ درصد وزنی در۰۳ گرم از پلیاستایرن گرید( ۰۳۳ نمونه)۹۰ و استئارت کلسیم۳/۰ درصد وزنی در ۰۳ گرم از پلیاستایرن گرید( ۰۳۳ نمونه ،)۹۰بهترین نتیجه( )A را از نقطهنظر لامپینگ از خود بروز دادند .برای بررسی اثرات مدت زمان ماندگاری پنتان به عنوان عامل فومکننده در داخل ساختار سلولی پلیاستایرن انبساطی، از آزمون کروماتوگرافی گازی نمونههای برتر آزمون کلوخهشدهگی) نمونههای ۹۰ ،۶و)۹۰ استفاده شد .این آزمون برای هر سه نمونهی فوق بعد از۰۳ روز از زمان تهیهی نمونهها و سپس۶۰ روز پس از ساخت نمونهها تکرار شدند .نتایج این آزمون نشان داد که میزان پنتان باقی مانده در نمونه۳/۰ درصد وزنی از استئارات روی در پلیاستایرن انبساطی گرید ۰/۹۹۶ ،۰۳۳درصد وزنی است که در مقایسه با هر دو استئارات روی و کلسیم در گرید ،۰۳۳که به ترتیب،۰/۰۰ و۰/۰۱ درصد گزارش شد، میزان پنتان باقیماندهی کمتری دارد
Text of Note
expansion process and this creates problems in downstream industries. Coating agents are used to prevent the beads from lumping together and to prevent the expanding agent from penetrating outside the cell structure. To evaluate the effect of coatings such as monoglycerol Stearate, Zinc Stearate and Calcium Stearate on reducing clumping, weight concentrations of 0.1, 0.3 and 0.5 of the above coatings, added to 50 grams of 300 and 400 grade polystyrene samples. A total of 18 samples, numbered from 1 to 18, were completely subjected to clumping test (lumping test). All samples were prepared at the same time and kept under the same conditions. Samples of 0.5 by weight of Zinc stearate in 50 g of polystyrene grade 300 (sample 6), Zinc stearate 0.5 by weight of 50 g of polystyrene grade 400 (sample 12) and Calcium stearate 0.3 by weight of 50 g of polystyrene grade 400 (sample 13) showed the best result (A) in terms of lamping. To investigate the effects of pentane shelf life as a foaming agent inside the expanded polystyrene cell structure, gas chromatography test of superior Lumping test samples (samples 6, 12 and 13) was used. This test was repeated for all three samples after 40 days from the time of sample preparation and then 65 days after sample making. The results of this test showed that the amount of pentane remaining in the sample of 0.5 by weight of Zinc stearate in expanded polystyrene grade 300, was 4.116 by weight compared to both zinc and calcium stearate in grade 400, which reported 4.57 and 5.58 , respectively, had less pentane content.-Expanded polystyrene is one of the products of Bead foaming technology. Production of polystyrene beads are categerized into different fractions such as 100, 200, 300, 400 and 500 based on the size of expansion polystyrene beads in the classification and sieving stage then after coating and packaging, products deliver to downstream companies. The presence of mineral contaminants, electrostatic charges and adhesion between expanded polystyrene beads causes the beads to accumulate in the pre
PARALLEL TITLE PROPER
Parallel Title
Study of Difficulties in the Expanded Poly styrene coating process and suggestion to overcome Lumping of final product
PERSONAL NAME - PRIMARY RESPONSIBILITY
عبدل زاده، علی اکبر
Abdolzadeh, Ali Akbar
PERSONAL NAME - SECONDARY RESPONSIBILITY
طهماسبپور، مریم، استاد راهنما
رنجبر، حیدر، استاد مشاور
ELECTRONIC LOCATION AND ACCESS
Public note
سیاه و سفید
نمایه‌سازی قبلی