مشخصه یابی لایه نفوذی تشکیل شده در اثر اکسایش حرارتی آلیاژ Ti-۶Al-۴V ELI دارای دانه بندی سطحی فوق ریز
General Material Designation
[پایاننامه]
Parallel Title Proper
Characterization of the oxide layer formed during thermal oxidation of ultrafine-Ti-۶Al-۴V ELI alloy with ultrafine-grained surface
First Statement of Responsibility
/سیما پرتوافکن
.PUBLICATION, DISTRIBUTION, ETC
Name of Publisher, Distributor, etc.
: مهندسی مواد
Date of Publication, Distribution, etc.
، ۱۴۰۱
PHYSICAL DESCRIPTION
Specific Material Designation and Extent of Item
۱۰۴ص.
Other Physical Details
:
GENERAL NOTES
Text of Note
زبان: فارسی
Text of Note
زبان چکیده: فارسی
NOTES PERTAINING TO PUBLICATION, DISTRIBUTION, ETC.
Text of Note
چاپی - الکترونیکی
NOTES PERTAINING TO PHYSICAL DESCRIPTION
Text of Note
مصور، جدول، نمودار
DISSERTATION (THESIS) NOTE
Dissertation or thesis details and type of degree
کارشناسی ارشد
Discipline of degree
مهندسی مواد- شناسایی و انتخاب مواد فلزی
Date of degree
۱۴۰۱/۰۳/۰۱
Body granting the degree
صنعتی سهند
SUMMARY OR ABSTRACT
Text of Note
هدف پژوهش حاضر، مطالعه رفتار اکسیداسیون دمای بالای آلیاژTi -۶Al-۴ ELI Vدر حضور اندازه دانهبندی سطحی فوقریز( إ m۱) <است .ساچمهپاشی پرانرژی به عنوان یکی از فرآیندهای تغییر شکل پلاستیک شدید سطحی، جهت ایجاد یک لایه سطحی فوقریز در آلیاژTi -۶Al-۴ ELI Vبه کار گرفته شد .این لایه سطحی با استفاده از میکروسکوپی الکترونی عبوری (TEM) و روش پراش پرتو ایکس سطحیXRD) - (GIتحلیل شد .این آزمونها حاکی از کاهش اندازه دانه سطحی تا مقادیر متوسط nm ۶۰ بود .افزون بر این، آزمون میکروسختی از لایههای سطحی نمونههای کار شده، حاکی از بروز تغییرات ریزساختاری متاثر از تغییر شکل تا عمق حدود إm۱۴۰ بود .افزایش قابل توجه مقادیر سختی سطح تا HV ۴۷۵ ~در مقایسه با حالت پایه (HV ۳۷۰) ~به کاهش شدید اندازه دانه و افزایش چگالی عیوب بلوری نسبت داده شد .تصاویر میکروسکوپی الکترونی روبشی نیز حاکی از افزایش تدریجی اندازه دانه از سطح تا لایههای زیرسطحی بود .آزمونهای آنالیز توزین حرارتی (TGA) و اکسیداسیون تک دما در دمای ۵۰۰، ۶۰۰ و ۷۰۰ درجه سانتیگراد( ۵، ۵۰ و ۱۰۰ ساعت) در اتمسفر هوا روی هر دو نمونه ساچمهپاشی شده و نشده انجام شد .نمونه دارای سطح ساچمهپاشی شده در ░ C۵۰۰ رفتار اکسیداسیون بهبود یافته از خود نشان میدهد .با توجه به نتایج آزمونهایSEM - FEو طیف سنجی نشری تخلیه نوری(GDOES) ، مشارکت قابل توجه تیتانیوم و آلومینیوم در شکلگیری لایه اکسید در این نمونه، به ایجاد یک لایه اکسیدی غنی از Al در نواحی بیرونی و داخلی و غنی از Ti در نواحی میانی منجر شد .تقابل نمونه ساچمهپاشی شده و نشده حاکی از آن بود که نواحی غنی از Al در نمونه ساچمهپاشی شده برخلاف نمونه ساچمهپاشی نشده به صورت یک لایه یکنواخت بودند .در دمای ░ C۶۰۰، اکسیداسیون نمونه ساچمهپاشی شده با تشکیل اکسیدهای محافظ همراه است .در حالی که نمونه ساچمهپاشی نشده قادر به تشکیل اکسید محافظ نبوده و دچار جدایش اکسید میشود .در دمای ░ C۷۰۰ عملا هر دو نمونه با جدایش شدید لایه اکسیدی، پدیده اکسیداسیون را تجربه میکنند .رفتار خوردگی نمونههای ساچمهپاشی شده( اکسید نشده و اکسید شده در ░ C۵۰۰) به صورت مقایسهای با همتای کار نشده آنها در محلول رینگر در دمای اتاق مورد بررسی قرار گرفت .نتایج آزمون پلاریزاسیون پتانسیودینامیک از کاهش دانسیته جریان روئینگی از مقدار متوسط إA/cm۲ ۵/۷ به مقدار إA/cm۲ ۰/۶در اثر کاهش اندازه دانه در نمونه کار شده حکایت دارند .افزون بر این، تحلیل امپدانس (EIS) نشان داد که حضور لایه اکسیدی بر سطح نمونه ساچمهپاشی شده، منجر به بهبود رفتار خوردگی و تشکیل لایه روئین پایدارتر در مقایسه با نمونه ساچمهپاشی نشده میشود.
Text of Note
A/cm2 due to a decrease in grain size in the treated sample. In addition, electrochemical impedance spectroscopy (EIS) showed that the improved corrosion behavior as a result of the formation of a more uniform and stable surface layer as the governing mechanismإ C) was compared with their untreated counterparts in Ringer's solution at room temperature. The results of potentiodynamic polarization test indicate a decrease in the passivity current density from an average of 5.7 A/cm2 to a mean value of 0.6 ░ C, both samples experience a catastrophic oxidation with severe spallation. The corrosion behavior of treated samples (non-oxidized and oxidized at 500 ░ C, oxidation of the treated sample is accompanied by the formation of protective oxides, while the non-treated sample is unable to form a protective oxide and separates from the oxide. At 700 ░ C. According to the results of FE-SEM and glow discharge optical emission spectroscopy (GDOES), the significant contribution of Cr and Al in the formation of the oxide layer in this sample led to formation an oxide layer rich in Al in the outer and inner regions, and rich in Ti in the middle regions. The Al-rich regions in the treated samples were uniformly layered in contrast to the non-treated specimen. At 600 ░ C (5, 50 and 100 h) in air for both treated and non-treated samples. The ultrafine-grained surface Ti6Al4V-ELI sample possessed an ideal oxidation behavior at 500 ░ The aim of the present study is to investigate the high temperature oxidation behavior of an ultrafine-grained surface Ti-6Al-4V ELI. High-energy shot peening, as a surface severe plastic deformation processe, was used to create an ultrafine-grained surface layer on Ti-6Al-4V ELI. This surface layer was analyzed using transmission electron microscopy (TEM) and surface X-ray diffraction (GI-XRD). These examinations showed a sharp reduction in the surface grain size to average values of 60 nm. Besides, microhardness measurements of the surface layers of treated samples revealed the process affected the surface layer up to depth of 140 m. A significant increase in surface hardness up to 475 HV compared to non-treated counterpart (370 HV) was attributed to the sharp decrease in grain size. Field-emission scanning electron microscopy (FE-SEM) images also showed a gradual increase in grain size from the surface to the subsurface layers. Thermal gravimetric analysis (TGA) and isothermal oxidation tests were performed at 500, 600 and 700
ba
PARALLEL TITLE PROPER
Parallel Title
Characterization of the oxide layer formed during thermal oxidation of ultrafine-Ti-۶Al-۴V ELI alloy with ultrafine-grained surface
TOPICAL NAME USED AS SUBJECT
ساچمهپاشی پرانرژی
اکسیداسیون دما بالا
سطح فوق ریزدانه
خوردگی
UNCONTROLLED SUBJECT TERMS
Subject Term
Ti6Al4V ELI; TEM; high-energy shot peening; high temperature oxidation; ultrafine-grained surface; corrosion
Subject Term
ساچمهپاشی پرانرژی، اکسیداسیون دما بالا، سطح فوق ریزدانه، خوردگی
PERSONAL NAME - PRIMARY RESPONSIBILITY
پرتوافکن، سیما
PERSONAL NAME - SECONDARY RESPONSIBILITY
توانگر، رضا، استاد راهنما
پورعلی، صادق، استاد مشاور
حجازی، سینا، استاد مشاور
ORIGINATING SOURCE
Country
ایران
Date of Transaction
20230913
LOCATION AND CALL NUMBER
Call Number
مواد ،۷۰۶۹۴ ،۱۴۰۱
ELECTRONIC LOCATION AND ACCESS
Host name
ژایلآ یترارح شیاسکا رثا رد هدش لیکشت یذوفن هیلا یبای هصخشم Ti-6Al-4V ELI زیر قوف یحطس یدنب هناد یاراد.pdf