عنوان

بررسی کارایی نانو ذرات دی اکسید تیتانیم تثبیت شده بر روی بسترهای مختلف در تصفیه فوتوکاتالیزی آبهای آلوده شده به مواد رنگزای آلی :بهینه سازی و مدل سازی فرآیند

‭۱۲۱۳پ‬

per

بررسی کارایی نانو ذرات دی اکسید تیتانیم تثبیت شده بر روی بسترهای مختلف در تصفیه فوتوکاتالیزی آبهای آلوده شده به مواد رنگزای آلی :بهینه سازی و مدل سازی فرآیند

/مهرانگیزفتحی نیا

تبریز : دانشگاه تبریز، دانشکده شیمی، گروه شیمی کاربردی

‮‭۱۲۱‬ص .‬

:مصور ، جدول ‮‭۳۰‬*‮‭۲۹‬ س .م - + لوح فشرده

چاپی

واژه نامه بصورت زیرنویس

کتابنامه ص .: ‮‭۱۱۵-۱۲۰‬

woven paper, their efficiency remained unchanged after four repetitions. Results from SEM images showed that the surface of ceramic plates before immobilization had more pores at nanoscale while glass surface was lumpy with fewer pores. oven papers, glass and ceramic plates during the photocatalytic process at different irradiation times were compared. The results indicated that decolorization efficiency for the mentioned substrates were 71 , 65.64 and 92.12 respectively. Also the electrical energy per order (EEO) values was investigated and results showed that amount of electrical energy consumed in the ceramic support were far less than the others. The efficiency and stability of the photocatalytic substrates on successive iterations during the four repetitions was studied. The results indicated that due to the high stability of TiO2 nanoparticles immobilized on glass and ceramic substrates in comparison with non-MS analysis verified the identity of intermediates and a reaction pathway based on them was proposed for BB3 degradation. The changes in the UVVis absorption spectrum of BB3 with non-woven papers, glass and ceramic plates allowed 86 , 100 and 100 mineralization after 12 h of the photocatalytic process. GC-1, and 200 min respectively. The degradation and mineralization of BB3 were followed by total organic carbon (TOC). The results of TOC measurements indicated that non-2, 100 mL min-1, 47.2 W m-1.he effect of dye molecular structure on photocatalytic degradation of BB3, AB92 and AG25 on immobilized glass plates was evaluated by response surface methodology (RSM). Results indicated that the photocatalytic decolorization efficiency of AB92 was higher than that of BB3 and AG25. The intermediate compounds of AB92 and AG25 degradation were identified by GCMS analysis and the relevant pathway was proposed. Modeling and optimization of photocatalytic degradation of BB3 on the three photocatalytic supports was investigated by RSM and effects of the four main independent parameters (initial dye concentration, UV light intensity, flow rate and reaction time) on the decolorization efficiency were studied. The optimum values which obtained by RSM for the mentioned parameters were 10 mg L-woven paper were investigated. Results showed the apparent firstorder rate constant (kapp) was dependent on the light intensity and initial concentration. It was also found that kapp increased with increasing photon flow and decreased with increasing of initial concentration of the dye. The kinetic modeling of the photocatalytic process indicated the reasonable correlation between the experimental and predicted apparent firstorder rate constant (R2=0.95). For describing the performance of photoreactor and flow pattern in the photoreactor residence time distribution (RTD) function was investigated. Residence time distribution curves revealed mixed flow pattern of the reactor at flow rate of 100 mL min-woven paper, glass plates and ceramic plates as photocatalyst supports were studied. The photocatalytic degradation kinetics of BB3 by non-In this study TiO2 nanoparticles were immobilized on to glass and ceramic plates via silane coupling agent. The mechanism of immobilization on the mentioned plates in different conditions was determined. Then, in order to investigate the efficiency of immobilized TiO2 nanoparticles, decolorization of dye solutions containing Basic blue 3 (BB3), Acid blue 92 (AB92) and Acid green 25 (AG25) using non

کارشناسی ارشد

شیمی-شیمی کاربردی

‮‭۱۳۸۹/۱۰/۲۵‬

تبریز : دانشگاه تبریز، دانشکده شیمی، گروه شیمی کاربردی

در کار پژوهشی حاضر ابتدا نانو ذرات ‮‭TiO۲‬ با استفاده اتصال دهنده سیلانی بر روی صفحات شیشه ای و سرامیکی تثبیت، و مکانیسم تثبیت نانو ذرات ‮‭TiO۲‬ بر روی بسترهای مذکور در شرایط مختلف ارائه شد .در ادامه به منظور بررسی کارایی نانو ذرات ‮‭TiO۲‬ تثبیت شده بر روی بسترهای فوتوکاتالیزوری، رنگزدایی مواد رنگزای آبی بازی‮‭۳‬ ، آبی اسیدی ‮‭۹۲‬ و سبز اسیدی ‮‭۲۵‬ از محلولهای آبی با استفاده از سه بستر فوتوکاتالیزوری الیاف کاغذی، صفحات شیشه ای و سرامیکی انجام گردید .همچنین با استفاده از بستر الیاف کاغذی مطالعات سینتیکی حذف فوتوکاتالیزوری ماده رنگزای آبی بازی ‮‭۳‬ مورد بررسی قرار گرفت .نتایج نشان داد که ثابت سرعت درجه اول ظاهری ‮‭(kapp)‬ تابعی از شدت نور ‮‭UV‬ و غلظت اولیه ماده رنگزا میباشد، بطوریکه ‮‭kapp‬ با افزایش شدت نور ‮‭UV‬ افزایش و با افزایش غلظت اولیه ماده رنگزا کاهش می یابد .مدلسازی سینتیکی فرآیند فوتوکاتالیزوری نشان داد که مقادیر ثابت سرعت پیش بینی شده توسط مدل مطابقت خوبی‮‭(۹۵/۰=(R۲‬ ، با نتایج تجربی دارد .به منظور توصیف عملکرد و مدل جریان در فوتوراکتور حاضر تابع توزیع زمانهای ماندگاری مورد بررسی قرار گرفت .نتایج نشان داد که عملکرد فوتوراکتور حاضر در شدت جریان‮‭۱۱۰۰ - mL min‬مشابه با راکتورهای با جریان مخلوط میباشد .با بکارگیری ‮‭TiO۲‬ تثبیت شده روی صفحات شیشه ای به بررسی تاثیر ساختار شیمیایی سه ماده رنگزای‮‭AB۹۲‬ ، ‮‭BB۳‬ و ‮‭AG۲۵‬ در راندمان رنگزدایی با استفاده از روش رویه پاسخ اقدام گردید .نتایج نشان داد که در مورد ماده رنگزای آبی اسیدی ‮‭۹۲‬ راندمان رنگزدایی بالاتر میباشد .با استفاده از روش آنالیز‮‭MS - GC‬اقدام به شناسایی محصولات میانی نموده و مکانیسم نشان دهنده مراحل معدنی شدن مواد رنگزای ‮‭AG۲۵‬و ‮‭AB۹۲‬بوسیله فرآیند فوتوکاتالیزوری پیشنهاد گردید.

TiO2 Nanoparticles

Immobilization of nanocatalyst

Kinetic modeling

Optimization

Water treatment